Concept 234 GraphiTex 7.0 Mil Matte White Polyester Wall Fabric 54 Inches x 100 Feet

Concept® 234 is a 7.0 mil premium white matte coated polyester fabric with an acrylic removable pressure sensitive adhesive backed by a 90# Layflat liner. The combination of fabric and adhesive allows removability of this product from normal wall surfaces. The 90# Layflat release liner provides excellent stability for processing using standard solvent, ecosolvent, UV curable and latex digital inks common to wide format digital printing systems.

Applications:   
Concept® 234 is designed for temporary application of decals and graphics to most types of painted interior walls. This includes most flat, semi gloss and gloss paint finishes. Decals may also be applied to sealed wall coverings. The surface must be smooth and clean prior to application. Not designed for coated/sealed/treated stainless steel, brass or bronze surfaces.

Film Thickness:  
 7.0 mils.
(Thickness variation +/- 10%)
 
Adhesive Thickness Side One:   
.8 to 1.2 mils.
(Thickness variation +/- 10%)

Liner Thickness Side One:   
6.7 mils.
(Thickness variation +/- 10%)

Temperature Ranges:   
Minimum application temperature +40°F.
Service temperature -40°F to +200 F.

Dimensional Stability:   
Good.

Adhesion:   
To standard test panels 4 to 12 oz. /in. Tested according to PSTC-101 Method A procedures with 24 hour dwell at 70°F and 50% relative humidity. Typical values. Individual values may vary. Bond to wall surfaces may vary. Test thoroughly before production.

Removability:   
Removable up to 6 months under normal interior exposure conditions and applications. Removal of wall fabric should be done at a 180° angle while pulling slowly against itself.

Storage Stability:   
6 months shelf life when stored at 70°F and 50% relative humidity.

Product Codes:   
Concept® 234-54 (54” x 100’)
Concept® 234-60 (60” x 100’)

Recommendations:   
Completely evaporate inkjet solvents before application. Failure to do so may facilitate solvent penetration resulting in product failure.